WC-CrC-Ni powders with wear resistance
Description
The WC-CrC-Ni powder product line is a series of agglomerated and sintered powders that offer an alternative to hard chromium plating. These powders are designed for use in low concentration acid/alkali environments at temperatures up to 200 ℃, and offer excellent anti-oxidation and wear resistance at temperatures as high as 750 ℃.
One of the key products in this line is KF-66, which contains 23% CrC and 7% Ni, with a particle size range of 15-45 μm and 10-38 μm. This product is highly versatile and can be used as a replacement for hard chromium plating in a variety of applications. It is particularly effective in low concentration acid/alkali environments at temperatures up to 200 ℃. In addition, KF-66 offers excellent resistance to oxidation and wear at temperatures up to 750 ℃.
Another important product in the WC-CrC-Ni powder line is KF-66, which contains 43% CrC and 14% Ni, with a similar particle size range of 15-45 μm and 10-38 μm. Like KF-66, this powder is an excellent alternative to hard chromium plating, and is highly effective in low concentration acid/alkali environments at temperatures up to 200 ℃.
In addition to their superior anti-oxidation and wear resistance, the WC-CrC-Ni powders offer several other advantages over hard chromium plating. For one, they are much easier to apply and require less specialized equipment. They are also more environmentally friendly, as they do not produce the same toxic byproducts as hard chromium plating.
Overall, the WC-CrC-Ni powder product line offers a highly effective alternative to traditional hard chromium plating. These powders provide superior anti-oxidation and wear resistance at high temperatures, making them ideal for a variety of industrial applications. Whether you are looking for a replacement for hard chromium plating or simply need a high-performance powder for use in harsh environments, the WC-CrC-Ni product line is an excellent choice.
Similar products
| Brand | Product Name | AMPERIT | METCO/AMDRY | WOKA | PRAXAIR | PAC |
| KF-66 | WC-20%CrC-7Ni | 551 | 37013702 | WC-7331356 | 8427 | |
| KF66A | 45WC-43%CrC-12Ni | Similar to 543 |
Specification
| Brand | Product Name | Particle Size (μm) | Chemistry (wt%) | Type | Apparent density | Flowability | Properties | Application | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Co | C | Fe | W | Cr | B | Si | Ni | ||||||||
| KF-65 | WC-10Co4Cr | 15-45, 10-38 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Sinter&Crush | 5.5-6.5g/cm3 | ≤25 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating; Petroleum, paper, general machinery | |||
| KF-65 | WC-10Co4Cr | 15-45,10-38,5-30 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating; Petroleum, paper, general machinery | |||
| KF-65 | WC-10Co4Cr | 5-25，5-15 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated and sintered | 3.5-4.8 g/cm3 | Stable feeding to powder feeder | HVOF,HVAF | Alternative hard chromium plating；Smoother surface, less or free post machining； | |||
| KF-60 | WC-12Co | 15-45，10-63 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Sinter&Crush | 5.5-6.5 g/cm3 | ≤25 s/50g | APS，HVOF | Wear resistance，Fretting wear resistance | ||||
| KF-60 | WC-12Co | 15-45，10-38，5-30 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVOF，HVAF | Wear resistance，Fretting wear resistance；general machinery | ||||
| KF-61 | WC-17Co | 15-45，10-38 | 15.5-17 | 4.5-5.1 | ≤0.8 | Bal. | Agglomerated and sintered | 3.5-5.5 g/cm3 | ≤25 s/50g | APS，HVOF，HVAF | Wear resistance，Fretting wear resistance，Better toughness； general machinery | ||||
| KF-62 | WC-25Co | 15-45，10-38 | 22-26 | 4.0-4.6 | ≤0.8 | Bal. | Agglomerated and sintered, Densification | 3.0-5.5 g/cm3 | ≤25 s/50g | APS, Detonation guns，cold spray | Fretting wear resistance，Better toughness | ||||
| KF-66 | WC-23%CrC-7Ni | 15-45，10-38 | 6.0-6.8 | ≤0.8 | Bal. | 16.5-20 | 5.5-7 | Agglomerated and sintered | 3.0-5.0 g/cm3 | ≤25 s/50g | APS，HVOF,HVAF | Alternative hard chromium plating；Used for low concentration acid/alkali environment at 200 ℃; Anti oxidation and wear resistance at 750 ℃ | |||
| KF-66 | 43WC-43%CrC-14Ni | 15-45,10-38 | 7.8-8.4 | ≤0.8 | Bal. | 35-38 | 12-14 | Agglomerated and sintered | 2.0-4.0 g/cm3 | ≤35 s/50g | APS，HVOF，HVAF | Alternative hard chromium plating Used for low concentration acid/alkali environment at 200 ℃ | |||
| KF-63 | WC-10Ni | 15-45,10-38 | 4.5-5.2 | ≤0.1 | Bal. | 8.5-10.5 | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS，HVF，HVAF | Non magnetic wear resistant coating. Better corrosion resistance | ||||
| KF-70 | Cr3C2-25NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 18-21.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃ | ||||
| KF-69 | Cr3C2-20NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃ | ||||
| KF-71 | Cr3C2-30NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated and sintered | ≥2.3 g/cm3 | Stable feeding to powder feeder | APS，HVOF | Anti oxidation and wear resistance at 815 ℃. Better toughness | ||||
| KF-60 | WC-12Co (Low Carbon) | 15-45, 20-53 | 10.5-12 | 4.0-4.4 | ≤0.8 | Bal. | Agglomerated and sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-10Co | 15-45,20-53,10-38 | 9-11 | 3.5-3.9 | Bal. | 1.4-1.7 | Agglomerated and sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | ||||
| KF-68 | WC-30WB-5Co5Cr | 15-45,20-53,10-38 | 4-6 | 3.5-3.9 | Bal. | 4-6 | 1.4-1.7 | Agglomerated and sintered | 3.0-4.9 g/cm3 | ≤30 s/50g | HVOF,HVAF | Used for Zn bath rolls in Continuous Galvanizing Lines | |||
| KF-300E | 35%WC-NiCrBSi | 15-53,45-104 | 2.5-3.2 | 1.0-2.6 | 32-35 | 7.5-9 | 1.5-1.9 | 2.0-2.7 | Bal. | WC and NiCrBSi forming alloy | 4.0-4.9 g/cm3 | ≤16 s/50g | HVOF，PS | Alternative Blended type WC+Ni60；Higher material utilization，Lower energy consumption, lower thermal impact；Used for glass mold | |
| KF-300F | 50%WC-NiCrBSi | 15-53,45-104 | 3.2-4.3 | 0.8-2.0 | 45-48 | 5.8-7.2 | 1.0-1.7 | 1.5-2.4 | Bal. | WC and NiCrBSi forming alloy | 5.0-7 g/cm3 | ≤16 s/50g | HVOF，PS | Alternative Blended type WC+Ni60；Higher material utilization，Lower energy consumption, lower thermal impact；Used for glass mold | |